NORYL GTX Resin GTX820 高耐热PPO+PA玻纤20％ NORYL GTX820 is a 20% glass reinforced grade with excellent chemical resistance in combination with high stiffness and heat resistance. TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yield, 5 mm/min 100 MPa ISO 527 Tensile Stress, break, 5 mm/min 95 MPa ISO 527 Tensile Strain, yield, 5 mm/min 2.5 % ISO 527 Tensile Strain, break, 5 mm/min 3.5 % ISO 527 Tensile Modulus, 1 mm/min 5700 MPa ISO 527 Flexural Stress, break, 2 mm/min 145 MPa ISO 178 Flexural Modulus, 2 mm/min 5200 MPa ISO 178 Hardness, H358/30 100 MPa ISO 2039-1 IMPACT Value Unit Standard Izod Impact, unnotched 80*10*4 +23°C 40 kJ/m ISO 180/1U Izod Impact, unnotched 80*10*4 -30°C 40 kJ/m ISO 180/1U Charpy Impact, notched, 23°C 7 kJ/m ISO 179/2C Charpy Impact, notched, -20°C 5 kJ/m ISO 179/2C Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm 50 kJ/m ISO 179/1eU Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm 40 kJ/m ISO 179/1eU THERMAL Value Unit Standard Thermal Conductivity 0.25 W/m-°C ISO 8302 CTE, 23°C to 60°C, flow 3.E-05 1/°C ISO 11359-2 CTE, 23°C to 60°C, xflow 7.E-05 1/°C ISO 11359-2 Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2 Vicat Softening Temp, Rate B/50 215 °C ISO 306 Vicat Softening Temp, Rate B/120 220 °C ISO 306 Relative Temp Index, Elec 120 °C UL 746B Relative Temp Index, Mech w/impact 60 °C UL 746B Relative Temp Index, Mech w/o impact 125 °C UL 746B PHYSICAL Value Unit Standard Mold Shrinkage on Tensile Bar, flow (2) (5) 0.3 - 0.7 % SABIC Method Density 1.25 g/cm ISO 1183 Water Absorption, (23°C/sat) 3.2 % ISO 62 Moisture Absorption (23°C / 50% RH) 1.08 % ISO 62 Melt Volume Rate, MVR at 280°C/5.0 kg 6 cm/10 min ISO 1133 FLAME CHARACTERISTICS Value Unit Standard UL Recognized, 94HB Flame Class Rating (3) 1.5 mm UL 94 UL Recognized, 94HB Flame Class Rating 2nd value (3) 3 mm UL 94 Oxygen Index (LOI) 26 % ISO 4589 Parameter Injection Molding Value Unit Drying Temperature 100 - 110 °C Drying Time 2 - 3 hrs Maximum Moisture Content 0.07 % Melt Temperature 280 - 300 °C Nozzle Temperature 270 - 290 °C Front - Zone 3 Temperature 280 - 300 °C Middle - Zone 2 Temperature 270 - 290 °C Rear - Zone 1 Temperature 260 - 280 °C Hopper Temperature 60 - 80 °C Mold Temperature 80 - 100 °C 标签： 中山市高耐热玻纤 中山市高耐热玻纤厂家 中山市高耐热玻纤厂家 供应用于阀门的高耐热PPO+PA玻纤20％
沙泊塑料有限公司（中山）